Stability and conductivity study of NH4PO3-PTFE composites at intermediate temperatures

Yinzhu Jiang, Xiaoxiang Xu, Rong Lan, Lei Zhang, Shanwen Tao

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

NH4PO3-PTFE inorganic-organic composite electrolytes were prepared. Their phase compositions, thermal stability and morphologies were investigated. The composites obtained demonstrate improved thermal stability comparing with commercial NH4PO3. The morphology of pellets under the same conditions shows the smoother and denser surface with more PTFE content added. The conductivity was measured by ac impedance spectroscopy under different atmospheres. The composites were found to exhibit a higher conductivity in humid 5% H2/Ar compared with open air atmosphere. A maximum conductivity of 2.3 mS/cm is obtained at 250 °C for NH4PO3-PTFE (volume ratio = 2:1) sample in humid 5% H2/Ar. © 2009 Elsevier B.V. All rights reserved.

Original languageEnglish
Pages (from-to)874-877
Number of pages4
JournalJournal of Alloys and Compounds
Volume480
Issue number2
DOIs
Publication statusPublished - 8 Jul 2009

Keywords

  • Composites
  • Conductivity
  • Electrolyte

Fingerprint Dive into the research topics of 'Stability and conductivity study of NH<sub>4</sub>PO<sub>3</sub>-PTFE composites at intermediate temperatures'. Together they form a unique fingerprint.

  • Cite this